Test | Method | Value/Unit |
---|---|---|
Flexural modulus | ISO 527 | 4400 MPa |
Tensile strength | ISO 527 | 61 MPa |
Elongation at break | ISO 527 | 3,4% |
Elongation at break | ISO 527 | 50 MPa |
Elongation at impact | ISO 527 | 3% |
Notched impact strength | ISO 179-1/1 eA | 4,4 kj/m2 |
Impact resistance | ISO 179-171 eU | 72kj/m2 |
Melt flow index (MFR) | ISO 1133 | 12 g/10 min |
Melting temperature | ISO 3146-C | 190–210 °C |
VICAT A (VST) | ISO 306 | 160 °C |
Dimensional stability (HDT/B) | ISO 75 | 115 °C |
Shrinkage | ISO 294-4 | 0,4% |
Tightness | ISO 1183 | 1,39 g/cm3 |